Two Component Solvent Free Epoxy Adhesive Comens Weld Dp1300t

Description.Comens Weld DP1300T is a two component, high quality without solvent epoxy adhesive, with subtle touch deformation, no flux during curing, very good infiltrative characters towards base material, good flame retardancy and good tensile, shock resistance, anti-peeling , adhesive tenacity strength. It can adapt to the high temperature environment, especially under the high temperature of 80ºC still maintain excellent mechanical properties.♦Micro thixotropic            ♦ High toughness                    ♦Pot life 55-65min♦Good performance at high temperatures       ♦very good infiltrative characters towards base materialMetal: aluminum, cold rolled steel, magnesium alloy, stainless steelComposite material: FRP,CFRPThermoplastic: PVC, acrylic, phenolic plastic, polycarbonate, fluoropolymerOther materials: fabric, foam, glass, wood, rubber Note: The following information and data are typical values under standard conditions, not as a basis for product acceptance.If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2 ° C and a humidity of 50 ± 5% RH.PropertyDP1300T PADP1300T PBMixedColorBlueYellowBlueDensity /g/cm31.3±0.11.1±0.11.2±0.1StatueLiquidLiquidLiquidViscosity /Pa.s60-9010-1530-60Pot life /min--55-65/24ºCFixed time10-12h(24ºC)/30min(60ºC)Curing time7d(24ºC)/2h(80ºC)Applicable temperature-40ºC~160ºCMixing ratioPA/PB=2:1.17(Volume ratio )PA/PB=2:1(Mass ratio)Note:  Operating time: refers to the time when DP1300T no longer has bonding ability after mixing 60g of A/B two components.Note: The following information and data are typical values under standard conditions, not as a basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2 ° C and a humidity of 50 ± 5% RH. ValueFailure modesConditions Shear strength /24ºC6061 aluminum /MPa20.4CF304 stainless steel /MPa22.6CF1010 cold rolled steel /MPa21.1CFFlat tensile strength /24ºC6061 aluminum /MPa4.0CFRoller peel strength /24ºC6061 aluminum /N.mm/mm55CFNote: Destructive form in the table CF = cohesive failure of the rubber layer          The test standard for shear strength: GB/T 7124          The test standard for flat tensile strength: GB/T 1452          The test standard for roller peel strength: GB/T 1457Note: The following information and data are typical values under standard conditions, not as a basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2 ° C and a humidity of 50 ± 5% RH.TemperatureShear strength/Retention rateFailure modes24ºC20.4/100%CF80ºC10.78/52.8%MM100ºC6.47/31.7%MM120ºC4.39/21.5%AF150ºC2.69/13.2%AFNote: Destructive form in the table CF = cohesive failure of the rubber layer,AF=glue interface disruption,MM=mixing damage;         The test standard for shear strength: GB/T 7124Note: The following information and data are typical values under standard conditions, not as a basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2 ° C and a humidity of 50 ± 5% RH.      Curing speed at 24ºC                         Curing speed at 60ºC                Note:In the figure, the abscissa is time and the ordinate is shear strength.               The test standard for shear strength: GB/T 7124Can withstand:Acid and base (PH3-10), hydrocarbons, brineCan't withstand:Polar solvent, strong acid and alkaliNote: The following information and data are typical values under standard conditions, not as a basis for product acceptance. If the test environment is not explicitly mentioned in the following tests, the test environment is unified to a temperature of 24 ± 2 ° C and a humidity of 50 ± 5% RH.ConditionsShear strength/Retention rateFailure modesRoller stripping strength/Retention rateFailure modesTemperature cycle 40 cycles14.72/72.1%CF29/52.8%MMNote: Destructive form in the table CF = cohesive failure of the rubber layer,AF=glue interface disruption,MM=mixing damage;         The test standard for shear strength: GB/T 7124         The test standard for roller peel strength is: GB/T 1457         The high and low temperature cycle adopts the standard: ISO9142Product specification: 400ml/tube; 3kg/group (PartA 1kg/pail*2, PartB 1kg/pail*1); 54kg/group (PartA 18kg/pail*2, PartB 18kg/pail*1)The recommended storage temperature is 8~25°C and the storage period is 12 months.Storage at 25°C helps to extend the shelf life of the product. Long-term exposure to room temperature and above will shorten the shelf life of the product. Do not expose the product to high temperature storage. Recommended storage environment: ventilated, dry and dark.When bonding, the surface to be bonded is wiped clean with a cleaning agent such as acetone or alcohol or gasoline to rem