E-Glass Fibreglass Direct Hooping Roving

Product DescriptionDirect Roving For Filament WindingDifferent E-glass direct roving applies in different production processes and are compatible with various resins, including polyester, vinyl ester, epoxy and polyurethane. It covers Pultrusion,Filament Winding,Weaving,LFT and CFRT.Direct Roving for Filament winding, is compatible with unsaturated polyester, polyurethane, vinyl ester, epoxy and phenolic resins.Main uses include manufacture of FRP pipes of various diameters, high-pressure pipes for petroleum transitions, pressure vessels, storage tanks, and, insulation materials such as utility rods and insulation tube.Product FeatureGood process performance and low fuzzCompatibillty with multiple of resin systemsGood mechanical propertiesComplete and fast wet-outExcellent acid corrosion resistanceProduct Parameters ItemLinear DensityResin CompatibilityFeaturesEnd UseBHFW-01D1200,2000,2400EPCompatible with epoxy resin, designed for filament winding process under high tensionused as reinforcement to manufacture high pressure pipe for petroleum transmissionBHFW-02D2000PolyurethaneCompatible with epoxy resin, designed for filament winding process under high tensionUsed to manufacture utility rodsBHFW-03D200-9600UP,VE,EPCompatible with resins; Low fuzz; Superior processing property; High mechanical strength of the composite productUsed to manufacture storage tanks and medial-pressure FRP pipes for water transmission and chemical corrosionBHFW-04D1200,2400EPExcellent electrical propertyUsed to manufacture hollow insulation pipeBHFW-05D200-9600UP,VE,EPCompatible with resins; Excellent mechanical properties of the composite productUsed to manufacture normal pressure-resistant FRP pipes and storage tanksBHFW-06D735UP,VE,UPExcellent process performance; Excellent chemical corrosion resistance, such as gas H2S corrosion etc; Excellent abrasion resistanceDesigned for RTP (reinforcement thermoplastics pipe) filament winding which requires acid resistance and abrasion resistance. It is suitable for application in spoolable piping systemsBHFW-07D300-2400EPCompatible with epoxy resin; Low fuzz; Designed for filament winding process under low tensionused as reinforcement of pressure vessel and high- and medial- pressure resistance FRP pipe for water transmissionIdentificationType of GlassEDirect RovingRFilament Diameter, μm13161717222431Linear Density, tex3002004006007351100 12002200240048009600  Technical ParametersLinear Density  (%)Moisture Content (%)Size Content     (%)Breakage Strength (N/Tex)ISO1889ISO3344ISO1887IS03341±5≤0.100.55±0.15≥0.40ApplicationIts excellent weaving property makes it suited for fiberglass product, such as roving cloth, combination mats, stitched mat,multi-axial fabric, geotextiles, molded grating.The end-use products are widely used in building & construction, wind power and yacht applications.Packaging & Shipping   StorageUnless otherwise specified, fiberglass products should be stored in a dry, cool and rain-proof area. It is recommended that the room temperature and humidity should be always maintained at 15 ºC~35 ºC and 35%~65% respectively. To ensure safety and avoid damage to the product, the pallets should not be stacked more than three layers high. When the pallets are stacked in 2 or 3 layers, care should be taken to correctly and smoothly move the top pallet. The product should be transferred to the workshop 24 hours before use to undergo conditioning.   PackagingThe product can be packed on pallet or in small cardboard boxes. Package height mm(in)260(10)260(10)Package inside diameter mm(in)160(6.3)160(6.3)Package outside diameter mm(in)270(10.6)310(12.2)Package weight kg (lb)15.6(34.4)22(48.5)  Number of layers3434Number of doffs per layer1612Number of doffs per pallet48643648Net weight per pallet kg (lb)750(1653.4)1000(2204.6)792(1764)1056(2328)  Pallet length mm (in)1120(44)1270(50)Pallet width mm (in)1120(44)960(37.8)Pallet height mm (in)940(37)1180(45)940(37)1180(46.5)Company Profile/* January 22, 2024 19:08:37 */!function(){function s(e,r){var a,o={};try{e&&e.split(",").forEach(function(e,t){e&&(a=e.match(/(.*?):(.*)$/))&&1