Aws Enife-C1 Eni-C1 Cast Iron Welding Electrodes Ni99 Ni55 Nickel Welding Rod Z308 Z408

Product DescriptionTyue Aws Enife-C1 Cast Iron Welding Electrode/Rod 3.2*350mmThe welding electrode/rod is Suitable for repairing or surfing cracked and worn parts made of gray cast iron or ncdular iron,as well as joining cast iron with dissimilar metals.It is machinable.Details about the Cast Iron Welding Electrode/Rod (AWS ENIFE-C1)Model Number: aws enife-c1 cast iron welding rodMaterial: Cast Iron welding rodLength: 300mm-500mmDiameter: 2.5mm 3.2mm 4.0mmApplication: All grades of castings, Pumps casing, gear housing, Engine blocksFeatures of welding rod1) Pure nickel core2) Strong reducing property3) Graphite type welding rod4) Weldment: No need to preheat, good crack resistibility and process-ability5) Both AC and DC applicable6) Relatively expensive7) Used for welding thin cast iron piece and repairing weldingSurfaces, such as the cast iron parts of cylinder covers,Engine bases, gearcases and lathe guide rails.Mechanical Properties of Deposited MetalTensile Strength Nmm2  ≥520(HV)   170-220DescriptionAn all position Medium heavy coated, graphite based cast iron electrodes. It deposits Nickel and Iron alloy weld metal, which is ductile and machineable, joining various types of cast Iron including nodular cast iron.Applications for welding rodThe cast iron welding rod is used for joining for non-ferrous and ferrous material, Heavy castings where machinability is required, Repair of broken castings, Engine heads, Pumps casing, ingot moulds.Our advantagesstable arc, little spatter, less smoke; higher deposition efficiency; excellent welding performance; easy restrike.Z208Z208 Cast Iron Welding ElectrodeAccord with:GB/T 10044 EZCDescription:Z208 is a graphitic type coating cast iron electrode with carbon steel core. Both AC and DC can be applied in welding. Weld seam metal has excellent crack resistibility. And its price is cheaper.Applications:It is used for repairing welding defects for gray cast iron.Chemical Composition of Deposited Metal: (%)  CMnSiSPFeStandard2.00-4.00≤0.752.50-6.50≤0.10≤0.15The restTypical2.700.404.200.0060.020 Recommended Current (AC or DC) Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)60-9090-120150-180190-220Attention:a.       welding electrodes must be baked for 1 hour at the temperature of 150ºC before welding.b.       For cast iron parts bearing impact stress, it is not good to use it.c.       For welding detects of small and thin cast iron parts fabricated by low steel, welding electrodes need not be preheated. For general welding pipes, welding electrodes should be preheated to around 400ºC, cool it after welding and the welding zone may be processed by cutting.Z308Z308 Cast Iron Welding ElectrodeAccord with:GB/T 10044 EZNi-1Equivalent norm: AWS A5.15 ENi-C1Description:Z308 is a covered welding electrode with pure nickel core and graphitic coating for cast iron. The Weld seam metal has excellent machinability and crack resistibility. Both AC and DC can be applied.Applications:It is used for repairing welding thin pieces and processing surface of cast iron, as well as important grey cast iron pieces, such as engine gear box, machining tools, guideway, etcChemical Composition of Deposited Metal: (%) CMnSiSNiFeOthersStandard≤2.0≤1.0≤2.50≤0.03≥90≤8.0≤1.0Typical0.590.071.500.004940.021 Recommended Current (AC or DC)Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)60-9090-110120-150150-180Attention:a.       welding electrodes must be baked for 1 hour at the temperature of 80-120ºC before welding.b.       Hammering the welded seam to dispel stress around the welding region and to avoid cracking.c.       Large current should be avoided in cold welding for cast iron, so as to reduce impurities of base metal to penetrate the weld seam and to reduce the width of the weld zone, and then to improve the ability of crack-resistance and capability of machine processing of the weld seam.Z408Z408 Cast Iron Welding ElectrodeAccord with:GB/T 10044 EZNiFe-1Equivalent norm: AWS A5.15 ENiFe-C1Description:Z408 is a graphitic (with strong reducing) type coating with Ni/Fe core welding electrodes for cast iron. It has features as follows: high toughness, excellent plasticity, low linear expansion coefficient, etc. Both AC and DC can be applied with welding.Applications:It is used for repairing welding important and high-toughness parts made of cast iron and modular iron, such as cylinder head, motor stand, gear wheel, etc.Chemical Composition of Deposited Metal: (%) CMnSiSNiFeAlCuStandard≤2.0≤2.5≤4.0≤0.0345-60The rest≤1.0≤2.50Typical0.700.241.000.006540.060.0540.054Recommended Current (AC or DC)Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)50-8080-110110-140150-180Attention:a.       welding electrodes must be baked for 1 hour at the temperature of 150ºC before welding.-------------------Our Other Welding Products-------------------If you are interested, please click on the below picture to enter the link   Welding ElectrodeCarbon Steel, Stainless Steel,Cast Iron etc.Nickel & Cobalt BasedHardfacing Weldi