Product DescriptionTyue Aws Enife-C1 Cast Iron Welding
Electrode/Rod
3.2*350mmThe welding electrode/rod is Suitable for repairing or surfing cracked and worn parts made of gray cast iron or ncdular iron,as well as joining cast iron with dissimilar metals.It is machinable.Details about the Cast Iron Welding Electrode/Rod (AWS ENIFE-C1)Model Number: aws enife-c1 cast iron welding rodMaterial: Cast Iron welding rodLength: 300mm-500mmDiameter: 2.5mm 3.2mm 4.0mmApplication: All grades of castings, Pumps casing, gear housing, Engine blocksFeatures of welding rod1) Pure nickel core2) Strong reducing property3) Graphite type welding rod4) Weldment: No need to preheat, good crack resistibility and process-ability5) Both AC and DC applicable6) Relatively expensive7) Used for welding thin cast iron piece and repairing weldingSurfaces, such as the cast iron parts of cylinder covers,Engine bases, gearcases and lathe guide rails.Mechanical
Properties of Deposited MetalTensile Strength Nmm2 ≥520(HV)
170-220DescriptionAn all position Medium heavy coated,
graphite based cast iron electrodes. It deposits Nickel and Iron
alloy weld metal, which is ductile and machineable, joining various
types of cast Iron including nodular cast iron.Applications for
welding rodThe cast iron welding rod is used for joining for
non-ferrous and ferrous material, Heavy castings where
machinability is required, Repair of broken castings, Engine heads,
Pumps casing, ingot moulds.Our
advantagesstable arc, little spatter, less smoke; higher deposition efficiency; excellent welding performance; easy restrike.Z208Z208
Cast Iron Welding ElectrodeAccord with:GB/T 10044
EZCDescription:Z208 is a graphitic type coating cast iron electrode
with carbon steel core. Both AC and DC can be applied in welding.
Weld seam metal has excellent crack resistibility. And its price is
cheaper.Applications:It is used for repairing welding defects for
gray cast iron.Chemical Composition of Deposited Metal:
(%) CMnSiSPFeStandard2.00-4.00≤0.752.50-6.50≤0.10≤0.15The
restTypical2.700.404.200.0060.020 Recommended Current (AC or
DC) Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)60-9090-120150-180190-220Attention:a.
welding electrodes must be baked for 1 hour at the temperature of
150ºC before welding.b. For
cast iron parts bearing impact stress, it is not good to use
it.c. For welding detects of
small and thin cast iron parts fabricated by low steel, welding
electrodes need not be preheated. For general welding pipes,
welding electrodes should be preheated to around 400ºC, cool it
after welding and the welding zone may be processed by
cutting.Z308Z308 Cast Iron Welding ElectrodeAccord with:GB/T 10044
EZNi-1Equivalent norm: AWS A5.15 ENi-C1Description:Z308 is a
covered welding electrode with pure nickel core and graphitic
coating for cast iron. The Weld seam metal has excellent
machinability and crack resistibility. Both AC and DC can be
applied.Applications:It is used for repairing welding thin pieces
and processing surface of cast iron, as well as important grey cast
iron pieces, such as engine gear box, machining tools, guideway,
etcChemical Composition of Deposited Metal:
(%) CMnSiSNiFeOthersStandard≤2.0≤1.0≤2.50≤0.03≥90≤8.0≤1.0Typical0.590.071.500.004940.021 Recommended
Current (AC or
DC)Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)60-9090-110120-150150-180Attention:a.
welding electrodes must be baked for 1 hour at the temperature of
80-120ºC before welding.b.
Hammering the welded seam to dispel stress around the welding
region and to avoid cracking.c.
Large current should be avoided in cold welding for cast iron, so
as to reduce impurities of base metal to penetrate the weld seam
and to reduce the width of the weld zone, and then to improve the
ability of crack-resistance and capability of machine processing of
the weld seam.Z408Z408 Cast Iron Welding ElectrodeAccord with:GB/T
10044 EZNiFe-1Equivalent norm: AWS A5.15 ENiFe-C1Description:Z408
is a graphitic (with strong reducing) type coating with Ni/Fe core
welding electrodes for cast iron. It has features as follows: high
toughness, excellent plasticity, low linear expansion coefficient,
etc. Both AC and DC can be applied with welding.Applications:It is
used for repairing welding important and high-toughness parts made
of cast iron and modular iron, such as cylinder head, motor stand,
gear wheel, etc.Chemical Composition of Deposited Metal:
(%) CMnSiSNiFeAlCuStandard≤2.0≤2.5≤4.0≤0.0345-60The
rest≤1.0≤2.50Typical0.700.241.000.006540.060.0540.054Recommended
Current (AC or
DC)Size(mm)2.5*3003.2*3504.0*4005.0*400Current(A)50-8080-110110-140150-180Attention:a.
welding electrodes must be baked for 1 hour at the temperature of
150ºC before welding.-------------------Our Other Welding
Products-------------------If you are interested, please click on
the below picture to enter the link Welding ElectrodeCarbon
Steel, Stainless Steel,Cast Iron etc.Nickel & Cobalt
BasedHardfacing Weldi
Related products about Aws Enife-C1 Eni-C1 Cast Iron Welding Electrodes Ni99 Ni55 Nickel Welding Rod Z308 Z408
-
Waste Tyre Plastic Recycling Machinery Machine Tire Crusher Production Line Rubber Crumb Grinding Machine Equipment Tire Shredder
-
Stretch Plastic Blowing Pet Bottle Making Blow Molding Machine Bottles Stretch Automatic Pet Bottle Blowing Machine
-
Waste Plastic Pet Bottle, Water Bottle Flake, PP/HDPE/LDPE PE Film Jumbo Woven Bags Plastic Crusher Machine, Plastic Crushing Washing Recycling Machine
-
Type 2 Wall-Mounted Electric Car Charging Station 7kw /11 Kwelectric Vehicle Charging Station Home Wallbox AC EV Charger Single Phase or 3three Phase
-
G-View G12W Wholesale Auto Car LED Headlight Bulb High Power H13 H11 9005 H7 H4 Car LED Headlights LED Car Lights
-
New Design Porcelain Round Plates Dinner Set for Wedding and Banquet
-
China 2023 New Design Super Soft 100% Polyester Microfiber Knitted Oversized Decoration Hoodie Blanket
-
Handmade Art Creative Materials Thickened White Paper Cup DIY Disposable Handmade Colored Paper Cup